I love the video Shaun. I really appreciate having that to add to this restoration. I'd love to know how you re-profiled the part after welding.
srcarr52
We can't stop here, this is bat country.
I did most of it with a roll lock sanding arbor on a right angle die grinder. A little was done with a stationary 6" belt sander and the intricate parts are with a foredom.
Your re-shaping work was spectacular! It looks as though it were machined! There are NO waves, divots, etc.
The welding is only half the work that goes into something like that.
Exactly!
srcarr52
We can't stop here, this is bat country.
I use some techniques I learned from repairing or cutting on tube race cars. Once you get close to the original surface you use roll lock sanding disks and keep it pressed flat and hard against the tube. Ensuring that you don't grind a divot in and that the surface is flat. The sanding disk will naturally pick on the high spot.
Dude has skillz.
Excellent work gentlemen!!
If you guys are having a hard time with the filler, there should be a glazing version. The glaze should be much thinner, like wood glue.
If you guys are having a hard time with the filler, there should be a glazing version. The glaze should be much thinner, like wood glue.
Jason Smoot
ArboristSite Operative
Subscribed.
MarylandGuy
ArboristSite Operative
From my perspective, the sanding part looks far more difficult. All I can say is wow.
It can be time consuming that is for sure.
srcarr52
We can't stop here, this is bat country.
I guess I'll have to make a video of that someday.
thats a very very nice restauration! The welding job on the one hand, the very positive way you handle and fix the discovered issues on the other hand,
lots of inspiration! Congratulations how you build such a nice saw in the end!
One question, I recently fixed a broken case with glass fiber and epoxy, and kept minor cracks in a sprocket
cover that might have been there for 40 year not affecting the performance...
For the cover, why did you select welding over a better job using fiber reinforced epoxy? Because you just
had a colleague with an amazing skillset? Because in terms of stability, the missing corner would not have to be
very resistant to mechanical stress...
and finally, how much original paint has to be sacrificed in case of welding? How big
would be the area that would burn away or change color? Sth. like 3 inch or more?
very nice, thanks a lot for showing all those details!
lots of inspiration! Congratulations how you build such a nice saw in the end!
One question, I recently fixed a broken case with glass fiber and epoxy, and kept minor cracks in a sprocket
cover that might have been there for 40 year not affecting the performance...
For the cover, why did you select welding over a better job using fiber reinforced epoxy? Because you just
had a colleague with an amazing skillset? Because in terms of stability, the missing corner would not have to be
very resistant to mechanical stress...
and finally, how much original paint has to be sacrificed in case of welding? How big
would be the area that would burn away or change color? Sth. like 3 inch or more?
very nice, thanks a lot for showing all those details!
LegDeLimber
Addicted to ArboristSite
Have you guys tried something like a toothpick?
Granted the hole has to be large enough for it to fit into.
Or something like a needle or small wire, with the tip a bit flattened.
Just work it almost like you're trying to scratch it out.
In places like that crack in the blasted part, I've used the small wire trick
to work glue into a crack or even a coarse textured surface.
Fubar
treehugger
- Joined
- Jan 27, 2015
- Messages
- 1,228
- Reaction score
- 1,356
killer saw ! didn't echo make a twin as well ? how many others made twins?
srcarr52
We can't stop here, this is bat country.
Fixed, heading your way soon brad.
Rx7man
Cattle Rubbing Post
Anyone else see the irony of a SOLO and a TWIN?
Nice saw, too bad I can't see the vid from here, I'll try and see it when I have real internet access.
Nice saw, too bad I can't see the vid from here, I'll try and see it when I have real internet access.
Im not really into the old saws brad but that thing is pretty damn cool
drf255
BAD CAD
Nice job Srcarr.
I see what you mean about Mag welding. Looks ALOT more forgiving than Aluminum.
So pretty much you use the laywire technique on AC?
Which filler rod and how many did you use?
The grinding and shaping look harder than the welding, but then again, that's what happens when you watch anyone whose good at it.
I see what you mean about Mag welding. Looks ALOT more forgiving than Aluminum.
So pretty much you use the laywire technique on AC?
Which filler rod and how many did you use?
The grinding and shaping look harder than the welding, but then again, that's what happens when you watch anyone whose good at it.